Adsorption and Photocatalytic Degradation of Methylene Blue on TiO2 Thin Films Impregnated with Anderson-Evans Al-Polyoxometalates: Experimental and DFT Study

Abstract

In this work, we fabricated a TiO2 thin film, and the same film was modified with an Anderson aluminum polyoxometalate (TiO2-AlPOM). Physical-chemical characterization of the catalysts showed a significant change in morphological and optical properties of the TiO2 thin films after surface modification. We applied the kinetic and isothermal models to the methylene blue (MB) adsorption process on both catalysts. The pseudo-second order model was the best fitting model for the kinetic results; qe (mg/g) was 11.9 for TiO2 thin films and 14.6 for TiO2-AlPOM thin films, and k2 (g mg-1 min-1) was 16.3 × 10-2 for TiO2 thin films and 28.2 × 10-2 for TiO2-AlPOM thin films. Furthermore, the Freundlich model was suitable to describe the isothermal behavior of TiO2, KF (5.42 mg/g), and 1/n (0.312). The kinetics of photocatalytic degradation was fitted using the Langmuir-Hinshelwood model; kap was 7 × 10-4 min-1 for TiO2 and 13 × 10-4 min-1 for TiO2-AlPOM. The comparative study showed that TiO2 thin films reach a 19.6% MB degradation under UV irradiation and 9.1% MB adsorption, while the TiO2-AlPOM thin films reach a 32.6% MB degradation and 12.2% MB adsorption on their surface. The surface modification improves the morphological, optical, and photocatalytic properties of the thin films. Finally, the DFT study supports all the previously shown results. © 2023 The Authors. Published by American Chemical Society